PERFORMANCE OF LATERITIC CONCRETE UNDER ENVIRONMENTAL HARSH CONDITION

Olubisi A. Ige

Abstract: This is an investigation of weathering characteristics of Laterized concrete with laterite-fine aggregate ratio as a factor. It was done with a view of ascertaining the suitability of laterite as aggregate substitutes at 0, 10, 20, 30 and 40% of fine aggregate used in the construction industry. The weathering characteristics were examined by conditioning laterized concrete cubes to varying temperatures, chemical and alternate wetting and drying, which all represent the operating weather conditions (wet and dry seasons) in tropics, including Nigeria. The mix proportion used was 1:2:4, the curing age of the laterized concrete was based on 28days curing age, while the compressive strength of the treated laterized concrete cubes was determined. The result of this research showed that the compressive strength of laterized concrete with laterite-fine aggregate ratio variation decreases when subjected to alternate wetting and drying and increases when subjected to magnesium sulphate (Mg2SO4). It was also discovered that a laterized concrete with a laterite-fine aggregate ratio of 20% conditioned to a temperature range of 100oC attained optimum compressive strength of 12.90Nmm-2

Keywords: Laterized Concrete, Comprehensive strength, Weathering Characteristics

DOI: https://doi.org/10.15623/ijret.2013.0208024